Simvastatin-enriched macro-porous chitosan-calcium-aluminate scaffold for mineralized tissue regeneration

Abstract The present study evaluated the odontogenic potential of human dental pulp cells (HDPCs) exposed to chitosan scaffolds containing calcium aluminate (CHAlCa) associated or not with low doses of simvastatin (SV). Chitosan scaffolds received a suspension of calcium aluminate (AlCa) and were then immersed into solutions containing SV. The following groups were established: chitosan-calcium-aluminate scaffolds (CHAlCa - Control), chitosan calcium-aluminate with 0.5 µM SV (CHAlCa-SV0.5), and chitosan calcium-aluminate with 1.0 µM SV (CHAlCa-SV1.0). The morphology and composition of the scaffolds were evaluated by SEM and EDS, respectively. After 14 days of HDPCs culture on scaffolds, cell viability, adhesion and spread, mineralized matrix deposition as well as gene expression of odontogenic markers were assessed. Calcium aluminate particles were incorporated into the chitosan matrix, which exhibited regular pores homogeneously distributed throughout its structure. The selected SV dosages were biocompatible with HDPCs. Chitosan-calcium-aluminate scaffolds with 1 µM SV induced the odontoblastic phenotype in the HDPCs, which showed enhanced mineralized matrix deposition and up-regulated ALP, Col1A1, and DMP-1 expression. Therefore, one can conclude that the incorporation of calcium aluminate and simvastatin in chitosan scaffolds had a synergistic effect on HDPCs, favoring odontogenic cell differentiation and mineralized matrix deposition.

Resumo O presente estudo avaliou o potencial odontogênico de células da polpa dental humana (HDPCs) em contato com scaffolds de quitosana contendo aluminato de cálcio (CHAlCa) associado ou não à baixas dosagens de sinvastatina (SV). Scaffolds de quitosana receberam uma suspensão de aluminato de cálcio e foram imersos em soluções contendo a droga. Foram estabelecidos três grupos experimentais: scaffolds de quitosana e aluminato de cálcio (CHAlCa - controle), scaffolds de quitosana-aluminato de cálcio com 0.5 µM SV (CHAlCa-SV0.5), e quitosana-aluminato de cálcio com 1.0 µM SV (CHAlCa-SV1.0). A morfologia e composição foram avaliados por MEV e EDS, respectivamente. Após 14 dias do cultivo das HDPCs sobre os scaffolds, foram avaliados a viabilidade celular, adesão e espalhamento, deposição de matriz mineralizada e expressão gênica de marcadores odontogênicos. Observou-se que as partículas de aluminato de cálcio foram incorporadas à matriz de quitosana, a qual exibiu poros regulares distribuídos por toda sua estrutura. As dosagens selecionadas de sinvastatina foram biocompatíveis com as HDPCs. A concentração de 1 µM de SV induziu intensa expressão de fenótipo odontoblástico pelas HDPCs, demonstrando aumento da deposição de matriz mineralizada e maior expressão de ALP, Col1A1 e DMP-1. Portanto, podemos concluir que a incorporação de aluminato de cálcio e sinvastatina em scaffolds de quitosana apresentou um efeito sinérgico nas HDPCs, favorecendo a diferenciação celular e deposição de matriz mineralizada.

Biostimulatory effects of simvastatin on MDPC-23 odontoblast-like cells

Abstract: The aim of this study was to evaluate the bioactivity and cytocompatibility of simvastatin (SV) applied to MDPC-23 odontoblast-like cells. For this purpose, MDPC-23 cells were seeded in 96-well plates and submitted to treatments with 0.01 or 0.1 μM of SV for 24 h, 72 h or continuously throughout the experimental protocol. The negative control group (NC) was maintained in DMEM. Cell viability (MTT), ALP activity (thymolphthalein monophosphate), and mineralized matrix deposition (alizarin red) were analyzed at several time points. The data were submitted to ANOVA and Tukey's test (α = 0.05). Although cell viability was observed in the groups treated with SV, these groups did not differ from the NC up to 7 days. There was a reduction in cell viability for the groups treated with 0.1 μM of SV for 72 h, and submitted to continuous mode after 14 days. A significant increase in ALP activity occurred in the group treated with 0.01 μM of SV for 24 h, compared with the NC; however, only the group treated with 0.1 μM of SV in continuous mode reduced the ALP activity, in comparison with the NC. After 14 days, only continuous treatment with 0.1 μM of SV did not differ from NC, whereas the other experimental groups showed increased mineralized matrix deposition. Thus, it was concluded that low concentrations of simvastatin were bioactive and cytocompatible when applied for short periods to cultured MDPC-23 odontoblast-like cells.